#CEREC TESSERA BLOCKS PC#
In contrast, Vita Suprinity PC had the highest strength in every aging condition among the glazing group.Ĭlinically Significant: Although all three materials might be suitable for single restorations, caution is needed when choosing material, especially as the rough surface from clinical adjustments may reduce its strength.
The fracture toughness for IPS e.max CAD was the highest with 1.97 ± 0.12 MPa.m1/2, CEREC Tessera 0.93 ± 0.05 MPa.m1/2, and Vita Suprinity PC 0.85 ± 0.08 MPa.m1/2.ĬONCLUSIONS: IPS e.max CAD polished outperformed Vita Suprinity PC and CEREC Tessera with respect to flexural strength under different aging conditions. Vickers Hardness was highest for CEREC Tessera with 7.19 ± 0.47 GPa, then Vita Suprinity PC at 7.05 ± 0.73 GPa, followed by IPS e.max CAD 5.79 ± 0.77 GPa. After thermal cycling and fatiguing, there were no significant effects in flexural strength for CEREC Tessera however, there was an increase in flexural strength for IPS e.max CAD and Vita Suprinity PC. The highest mean flexural strength for static was IPS e.max CAD 385.91 ± 46.23 MPa, then Vita Suprinity PC glazed 355.72 ± 72.44 MPa, followed by CEREC Tessera glazed 323.40 ± 61.01 MPa. RESULTS: Significant differences were observed in the mean of biaxial flexural strength between the three glass-ceramics materials. Data were analyzed using one-way ANOVA test or least square regression (α = 0.05) and the post hoc Tukey HSD test. Additionally, surface topography and crystal microstructure analysis by SEM and crystallographic structural analysis by X-ray diffraction were done. Also, surface roughness was measured for each group using a stylus contact profilometer. Vickers indentation was performed to test microhardness and fracture toughness. CEREC Tessera blocks are a glass-containing material and can be etched with hydrofluoric acid for adhesive bonding with resin cements. For example, the grinding time for molar crowns is between 13 and 16 minutes when the inLab MC XL or CEREC Primemill grinding and milling unit is used. Grinding times depend strongly on the kind of restoration. Thermal artificial aging cycling was from 5° to 55☌, while fatigue was used for about 20% of the static failure load for 200,000 cycles. CEREC Tessera blocks are grinded in their fully crystallized tooth colored state.
#CEREC TESSERA BLOCKS ISO#
The biaxial flexural strength test was preformed according to ISO 6872-2015 using an Instron universal testing machine. Specimens were randomly assigned for the biaxial flexural strength test then each group was tested under three conditions post-treatment: (1) static, (2) thermal cycling for 5000 cycles, and (3) cyclic loading at 200,000 cycles. Specimens were divided into three groups (1) glaze control, (2) polish only, and (3) ground after manufacturer glaze. MATERIALS AND METHODS: For each material, CAD/CAM blocks were sectioned into a total of N=108 (n=12 per group) test discs with a diameter of 11.3 mm core drill and used the precision saw machine. It’s the trifecta for single-visit successĬontains 2 each: A1 (MT), A2 (MT & HT), A3 (MT & HT), A3.5 (MT).OBJECTIVES: To evaluate the mechanical and physical properties of three glass-ceramic CAD/CAM systems Vita Suprinity PC (Vita ZahnFabrik), Cerrec Tessera (Dentsply-Sirona), and IPS e.max CAD (Ivoclar Vivadent).
Up to 32% higher biaxial strength for restoration longevity.Īnd up to 44% faster total processing time for greater patient satisfaction and a more profitable procedure. Now, there's one Choice for Beauty, Strength and Speed without unwanted Trade-Offs: CEREC Tessera CAD/CAM blocks provide outstanding esthetics for a truly tooth-like restoration. These trade-offs force unwanted decisions-from not using stains in order to fire faster to complicating inventory and processing protocols by keeping two or more block materials in stock. CEREC Tessera - Advanced Lithium Disilicate (ALD)įor single-visit indirect restorations, clinicians have grown accustomed to making trade-offs.
0 kommentar(er)